Сталь  1.2067 / 102Cr6 / 9Х2 

Химический состав стали 102Cr6 (1.2067)

C	Si	Mn	Ni	P	S	Cr	Mo
0.95 — 1.1	0.15 — 0.35	0.2 — 0.4	max   0.4	max   0.025	max   0.025	1.35 — 1.6	max   0.1

Механические свойства стали   102Cr6 (1.2067)

Nominal thickness (mm):	0.3 — 3
Rm — Tensile strength (MPa) (+A)	750

Nominal thickness (mm):	0.3 — 3
Rm — Tensile strength (MPa) (+QT)	1300-2100

Nominal thickness(mm):	0.3 — 3
Rp0.2 0.2% proof strength (MPa) (+A)	590

Nominal thickness (mm):	0.3 — 3
A — Min. elongation Lo = 80 mm (%) (+A)	11

Vickers hardness  ( HV):   (+A)	235
Vickers hardness  ( HV):   (+QT)	405 — 630
Brinell hardness   (HB):   (+A)	223