Инструментальная листовая сталь 1.2067 / 102Cr6 / ст 9Х2
Химический состав стали 102Cr6 (1.2067)
C
|
Si
|
Mn
|
Ni
|
P
|
S
|
Cr
|
Mo
|
0.95 — 1.1
|
0.15 — 0.35
|
0.2 — 0.4
|
max 0.4
|
max 0.025
|
max 0.025
|
1.35 — 1.6
|
max 0.1
|
Механические свойства стали 102Cr6 (1.2067)
Nominal thickness (mm):
|
0.3 — 3
|
|
|
Rm — Tensile strength (MPa) (+A)
|
750
|
Nominal thickness (mm):
|
0.3 — 3
|
|
|
Rm — Tensile strength (MPa) (+QT)
|
1300-2100
|
Nominal thickness(mm):
|
0.3 — 3
|
|
|
Rp0.2 0.2% proof strength (MPa) (+A)
|
590
|
Nominal thickness (mm):
|
0.3 — 3
|
|
|
A — Min. elongation Lo = 80 mm (%) (+A)
|
11
|
Vickers hardness ( HV): (+A)
|
235
|
Vickers hardness ( HV): (+QT)
|
405 — 630
|
Brinell hardness (HB): (+A)
|
223
|